An article Synthesis and characterization of novel polyimides based on 10,10-bis[4-(4-aminophenoxy)-3-methylphenyl]-9(10H)-anthrone WOS:000544441700006 published article about LOW-DIELECTRIC-CONSTANT; T-G; IMIDE)S; DIANHYDRIDE; POLYAMIDES; DIAMINE; PROPANE in [Kuang, Lu; Zhong, Ming; Sang, Xiao-Yan; Huang, Zhen-Zhong] Jiangxi Normal Univ, Key Lab Funct Small Organ Mol, Minist Educ, Nanchang 330022, Jiangxi, Peoples R China in 2020, Cited 30. The Name is Anthrone. Through research, I have a further understanding and discovery of 90-44-8. Safety of Anthrone
10,10-Bis[4-(4-aminophenoxy)-3-methylphenyl]-9(10H)-anthrone, as a novel aromatic diamine, was synthesized from anthrone by three-step process. A series of polyimides containing methyl substituents and 9(10H)-anthrone pendant groups was prepared from this diamine with various aromatic dianhydridesviathe poly(amic acid) (PAA) precursors and subsequent thermal or chemical imidization procedure. Inherent viscosities of PAAs are between 0.87 and 1.58 dL/g, and the corresponding polyimides have the weight-average molecular weight and number-average molecular weight in the range of 49,400-64,200 and 28,700-37,700, respectively. Most of the polyimides obtained through the chemical cyclodehydration method are soluble in NMP, DMF, DMAc, Py andm-cresol at room temperature. These polyimides have glass transition temperatures of 289-313 degrees C, 10% weight loss temperatures of 484-524 degrees C, char yields of 55-63% at 800 degrees C, and temperature at the maximum-rate degradation of 560-584 degrees C in nitrogen, respectively. The polyimide films obtained through the thermal imidization have tensile strength of 76.43-119.74 MPa, elongation at break of 6.93-12.33%, and tensile modulus of 1.91-2.38 GPa.
Bye, fridends, I hope you can learn more about C14H10O, If you have any questions, you can browse other blog as well. See you lster.. Safety of Anthrone
Reference:
Thiomorpholine – Wikipedia,
,Thiomorpholine | C4H9NS – PubChem